Recycling of constructional plastics with additives of exhausted polyethylene

Abstract

RACT Received polymeric materials with the use of wasted polyethylene of РЕ-500 and РЕ-1000 grades can serve, as construction materials at regimes, which correspond to characteristics of new PCM. Presence of carbon fibers in composites such as UPА-6-30+РЕ-500 (10%) and UPA-6-30+РЕ-1000 (10%) allows applying details, made of these materials without normative greasings. The use of waste polyethylene of РЕ mark decreases physicomechanical characteristics in received PCM with the exception of impacting viscosity. It is shown that such an indicator as the stress of the boundary of the volume of compression is high (about 100 MPa), which indicates the possibility of using PCM data, for example, for bearings of parallelogram mechanisms of sewing machines, where the pressure value is within the range of 23 to 30 MPa. RACT Отримані полімерні матеріали з використанням відпрацьованого поліетилену марок РЕ-500 і РЕ-1000 можуть служити конструкційними матеріалами при режимах, що відповідають характеристикам нових ПКМ. Наявність вуглецевих волокон у композитах УПА-6-30+РЕ-500 (10%) та УПА-6-30+РЕ-1000 (10%) дозволяє застосовувати деталі з цих матеріалів без нормативних змащувань. Використання відпрацьованого поліетилену марки РЕ знижує фізико-механічні характеристики отриманого ПКМ, за винятком впливу на в'язкість. Показано, що такий показник, як напруга межі об’єму стиснення, є високим (близько 100 МПа), що свідчить про можливість використання даних ПКМ, наприклад, для підшипників паралелограмних механізмів швейних машин, де тиск значення знаходиться в діапазоні від 23 до 30 МПа.